logfile

   1 it's never too late to start a logfile ...
   2                                #######
   3
   4
   5 23.02.2009:
   6 -----------
   7
   8 ./posic_2009_02/saves/c_in_si_prec_2050_01
   9 ./posic_2009_02/saves/c_in_si_prec_2050_02 WARNING: bullshit notation! see below
  10 ./posic_2009_02/saves/c_in_si_prec_2050_03
  11
  12  c in sphere of r = 2.5 nm at 01 = 2050 02 = 1650 03 = 1250 celsius
  13
  14 local: sic_prec_08-tup1250 / 1650 / 2050
  15
  16  sic prec at 1250 / 1650 / 2050 celsius
  17
  18 ./posic_2009_02/saves/c_in_si_prec_04
  19 ./posic_2009_02/saves/c_in_si_prec_05
  20 ./posic_2009_02/saves/c_in_si_prec_06
  21
  22  like first three, using tersoff <- TODO
  23
  24 TODO: kleine si mit genausoviel c ins
  25       c in groesseres gebiet (tot oder so?)
  26
  27 19.02.2009:
  28 -----------
  29
  30 local: sic_prec_08*
  31
  32  sic in si + anneals ...
  33
  34 09.02.2009:
  35 -----------
  36
  37 ./posic_2009_01/saves/c_in_si_prec_1650-2150_v2_04
  38
  39  tersoff instead of albe, cr = 1.5 angstrom, insertion into sphere r=2.5
  40
  41 06.02.2009:
  42 -----------
  43
  44 adapted parcas albe sic parameters, dcut of si-1 unmodified!
  45
  46 13.01.2009:
  47 -----------
  48
  49 ./posic_2009_01/saves/c_in_si_prec_1650-2150_v2_03
  50
  51  as 02, but cr of Si-C increased to 1.9
  52
  53 12.01.2009:
  54 -----------
  55
  56 ./posic_2009_01/saves/c_in_si_prec_1650-2150_v2_02
  57
  58  as 01, but: c insertion cr check for another c atom increased to 2.7 angstrom
  59
  60 08.01.2009:
  61 -----------
  62
  63 INS_SPHERE implemented
  64
  65 ./posic_2009_01/saves/c_in_si_prec_1650-2150_v2_01
  66
  67  316 x 10 C -> Si, v2: sphere r=2.5 nm, t=1650(+500)