it's never too late to start a logfile ...
                               #######


23.02.2009:
-----------

./posic_2009_02/saves/c_in_si_prec_2050_01
./posic_2009_02/saves/c_in_si_prec_2050_02 WARNING: bullshit notation! see below
./posic_2009_02/saves/c_in_si_prec_2050_03

 c in sphere of r = 2.5 nm at 01 = 2050 02 = 1650 03 = 1250 celsius

local: sic_prec_08-tup1250 / 1650 / 2050

 sic prec at 1250 / 1650 / 2050 celsius

./posic_2009_02/saves/c_in_si_prec_04
./posic_2009_02/saves/c_in_si_prec_05
./posic_2009_02/saves/c_in_si_prec_06

 like first three, using tersoff <- TODO

TODO: kleine si mit genausoviel c ins
      c in groesseres gebiet (tot oder so?)

19.02.2009:
-----------

local: sic_prec_08*

 sic in si + anneals ...

09.02.2009:
-----------

./posic_2009_01/saves/c_in_si_prec_1650-2150_v2_04

 tersoff instead of albe, cr = 1.5 angstrom, insertion into sphere r=2.5

06.02.2009:
-----------

adapted parcas albe sic parameters, dcut of si-1 unmodified!

13.01.2009:
-----------

./posic_2009_01/saves/c_in_si_prec_1650-2150_v2_03

 as 02, but cr of Si-C increased to 1.9

12.01.2009:
-----------

./posic_2009_01/saves/c_in_si_prec_1650-2150_v2_02

 as 01, but: c insertion cr check for another c atom increased to 2.7 angstrom

08.01.2009:
-----------

INS_SPHERE implemented

./posic_2009_01/saves/c_in_si_prec_1650-2150_v2_01

 316 x 10 C -> Si, v2: sphere r=2.5 nm, t=1650(+500)