logfile

   1 it's never too late to start a logfile ...
   2                                #######
   3
   4
   5 06.04.2009:
   6 -----------
   7
   8 ./posic_2009_02/saves/c_in_si_prec_10 <- 2050
   9 ./posic_2009_02/saves/c_in_si_prec_11 <- 1650
  10 ./posic_2009_02/saves/c_in_si_prec_12 <- 1250
  11
  12  like 07, 08, 09 but using tersoff = tersoff + total volume
  13
  14 ./posic_2009_02/saves/c_in_si_prec_07_cnt0k
  15 ./posic_2009_02/saves/c_in_si_prec_09_cnt0k
  16
  17  continued (from 23.02.09), cooling down to 0K
  18
  19 23.02.2009:
  20 -----------
  21
  22 ./posic_2009_02/saves/c_in_si_prec_2050_01
  23 ./posic_2009_02/saves/c_in_si_prec_2050_02 WARNING: bullshit notation! see below
  24 ./posic_2009_02/saves/c_in_si_prec_2050_03
  25
  26  c in sphere of r = 2.5 nm at 01 = 2050 02 = 1650 03 = 1250 celsius
  27
  28 local: sic_prec_08-tup1250 / 1650 / 2050
  29
  30  sic prec at 1250 / 1650 / 2050 celsius
  31
  32 ./posic_2009_02/saves/c_in_si_prec_04
  33 ./posic_2009_02/saves/c_in_si_prec_05
  34 ./posic_2009_02/saves/c_in_si_prec_06
  35
  36  like first three, using tersoff <- TODO
  37
  38 ./posic_2009_02/saves/c_in_si_prec_07 <- 2050
  39 ./posic_2009_02/saves/c_in_si_prec_08 <- 1650
  40 ./posic_2009_02/saves/c_in_si_prec_09 <- 1250
  41
  42  like first three (albe!) into total volume
  43
  44 TODO: - kleine si mit genausoviel c ins
  45       - c in groesseres gebiet (tot oder so?)
  46       - c in grosses gebiet + 'mehr' c
  47
  48 19.02.2009:
  49 -----------
  50
  51 local: sic_prec_08*
  52
  53  - sic in si, free run for 2ps, tctrl to 23 celsius
  54  - more tctrl and annealing
  55
  56 09.02.2009:
  57 -----------
  58
  59 ./posic_2009_01/saves/c_in_si_prec_1650-2150_v2_04
  60
  61  tersoff instead of albe, cr = 1.5 angstrom, insertion into sphere r=2.5
  62
  63 06.02.2009:
  64 -----------
  65
  66 adapted parcas albe sic parameters, dcut of si-1 unmodified!
  67
  68 13.01.2009:
  69 -----------
  70
  71 ./posic_2009_01/saves/c_in_si_prec_1650-2150_v2_03
  72
  73  as 02, but cr of Si-C increased to 1.9
  74
  75 12.01.2009:
  76 -----------
  77
  78 ./posic_2009_01/saves/c_in_si_prec_1650-2150_v2_02
  79
  80  as 01, but: c insertion cr check for another c atom increased to 2.7 angstrom
  81
  82 08.01.2009:
  83 -----------
  84
  85 INS_SPHERE implemented
  86
  87 ./posic_2009_01/saves/c_in_si_prec_1650-2150_v2_01
  88
  89  316 x 10 C -> Si, v2: sphere r=2.5 nm, t=1650(+500)