logfile

   1 it's never too late to start a logfile ...
   2                                #######
   3
   4
   5 05.06.2009:
   6 -----------
   7
   8 local: c_in_si_mig_01
   9
  10 migratin of defects tests
  11
  12 06.05.2009:
  13 -----------
  14
  15 local: si_0k, si_20, si_1250, si_2050
  16        c_0k, c_20, c_1250, c_2050
  17        sic_0k, sic_20, sic_1250, sic_2050
  18
  19  fully relaxed si, c or sic at given temperature, using albe pot
  20
  21        ... _tersoff
  22
  23  same, using tersoff pot
  24
  25        ... _check
  26
  27  same, without tp-ctrl, to check conservation of energy (both, tersoff an albe)
  28
  29 04.05.2009:
  30 -----------
  31
  32 local: c_in_si_prec_01
  33
  34  3x3 lattice si, insertion of same amount of carbon at 2050 celsius, relax 1 ns
  35
  36 06.04.2009:
  37 -----------
  38
  39 ./posic_2009_02/saves/c_in_si_prec_10 <- 2050
  40 ./posic_2009_02/saves/c_in_si_prec_11 <- 1650
  41 ./posic_2009_02/saves/c_in_si_prec_12 <- 1250
  42
  43  like 07, 08, 09 but using tersoff = tersoff + total volume
  44
  45 ./posic_2009_02/saves/c_in_si_prec_12_cnt0k
  46
  47  continued, cooling down to 0k
  48
  49 ./posic_2009_02/saves/c_in_si_prec_07_cnt0k
  50 ./posic_2009_02/saves/c_in_si_prec_09_cnt0k
  51
  52  continued (from 23.02.09), cooling down to 0K
  53
  54 23.02.2009:
  55 -----------
  56
  57 ./posic_2009_02/saves/c_in_si_prec_2050_01
  58 ./posic_2009_02/saves/c_in_si_prec_2050_02 WARNING: bullshit notation! see below
  59 ./posic_2009_02/saves/c_in_si_prec_2050_03
  60
  61  c in sphere of r = 2.5 nm at 01 = 2050 02 = 1650 03 = 1250 celsius
  62
  63 local: sic_prec_08-tup1250 / 1650 / 2050
  64
  65  sic prec at 1250 / 1650 / 2050 celsius
  66
  67 ./posic_2009_02/saves/c_in_si_prec_04
  68 ./posic_2009_02/saves/c_in_si_prec_05
  69 ./posic_2009_02/saves/c_in_si_prec_06
  70
  71  like first three, using tersoff <- TODO
  72
  73 ./posic_2009_02/saves/c_in_si_prec_07 <- 2050
  74 ./posic_2009_02/saves/c_in_si_prec_08 <- 1650
  75 ./posic_2009_02/saves/c_in_si_prec_09 <- 1250
  76
  77  like first three (albe!) into total volume
  78
  79 TODO: - kleine si mit genausoviel c ins
  80       - c in groesseres gebiet (tot oder so?)
  81       - c in grosses gebiet + 'mehr' c
  82
  83 19.02.2009:
  84 -----------
  85
  86 local: sic_prec_08*
  87
  88  - sic in si, free run for 2ps, tctrl to 23 celsius
  89  - more tctrl and annealing
  90
  91 09.02.2009:
  92 -----------
  93
  94 ./posic_2009_01/saves/c_in_si_prec_1650-2150_v2_04
  95
  96  tersoff instead of albe, cr = 1.5 angstrom, insertion into sphere r=2.5
  97
  98 06.02.2009:
  99 -----------
 100
 101 adapted parcas albe sic parameters, dcut of si-1 unmodified!
 102
 103 13.01.2009:
 104 -----------
 105
 106 ./posic_2009_01/saves/c_in_si_prec_1650-2150_v2_03
 107
 108  as 02, but cr of Si-C increased to 1.9
 109
 110 12.01.2009:
 111 -----------
 112
 113 ./posic_2009_01/saves/c_in_si_prec_1650-2150_v2_02
 114
 115  as 01, but: c insertion cr check for another c atom increased to 2.7 angstrom
 116
 117 08.01.2009:
 118 -----------
 119
 120 INS_SPHERE implemented
 121
 122 ./posic_2009_01/saves/c_in_si_prec_1650-2150_v2_01
 123
 124  316 x 10 C -> Si, v2: sphere r=2.5 nm, t=1650(+500)